| Waterbase Sheetfed | |||||||||
| Product Reference | |||||||||
| Y=Yes N=No | |||||||||
| Relative - 1 to 10 best | |||||||||
| Drying | Rub | Adhesion to | Viscosity | ||||||
| Speed | Two | Resist. | Film/Foil/Glue | #3 S90 Zahn@70ÁF | Flexibility | ||||
| Product Code | Product Descriptiom | (relative) | Sided | (relative) | (relative) | (seconds) | (seconds) | ||
| Workhorse/Gen. Purpose | |||||||||
| CK-3149RR-2 | Excellent Gloss & Rub | 9 | Y | 9 | 9 | 20-25 | |||
| CK-4312WT | Economical | 9 | Y | 9 | 8 | 18-22 | |||
| CK-4200 | Excellent Gloss | 9 | Y | 9 | 8 | 22-27 | |||
| CK-4311PG | Economical | 8 | N | 7 | 9 | 18-22 | |||
| High Rub | |||||||||
| CK-4900 | High Gloss, Highest Rubs | 9 | Y | 10 | 7 | 17-21 | 17-21 seconds | ||
| CK-4851 | Gloss/Rub | 9 | Y | 9 | 8 | 19-24 | 19-24 seconds | ||
| CK-3149RR-3 | Gloss/Rub | 9 | Y | 9 | 8 | 20-25 | 20-25 seconds | ||
| CK-4315UF | Faster dry | 10 | Y | 10 | 6 | 22-27 | 22-27 seconds | ||
| Heat Resistant | |||||||||
| CK-608LW-3 | Highest Heat | 9 | Y | 9 | 8 | 20-25 | 20-25 seconds | ||
| CK-608LW-2 | Higher Gloss | 8 | N | 9 | 8 | 20-24 | 20-24 seconds | ||
| Water & Grease Resist. | |||||||||
| CK-42-18SR | Excellent Grease/Water | 10 | N | 8 | 6 | 18-25 | 18-25 seconds | ||
| CK-43P-23L | Lower Slide | 10 | Y | 8 | 6 | 20-25 | 20-25 seconds | ||
| High Gloss | |||||||||
| CK-49HG-1 | Highest Gloss | 5 | N | 8 | 8 | 22-27 | 22-27 seconds | ||
| CK-49HG-2 | Gloss | 6 | N | 7 | 8 | 22-27 | 22-27 seconds | ||
| UV - Primers | |||||||||
| CK-1250 | Best Adhesion | 9 | N | 5 | 10 | 22-25 | 22-25 seconds | ||
| CK-4333-3 | Non Porous W/T | 10 | Y | 9 | 8 | 18-25 | 18-25 seconds | ||
| Film, Poly, Metalized | |||||||||
| CK-4315UF | Film,Poly Best Rub | 10 | Y | 10 | 6 | 22-27 | 22-27 seconds | ||
| CK-4315SF | Film,Poly | 10 | Y | 9 | 7 | 22-27 | 22-27 seconds | ||
| CK-43-1208 | Metalized /// Clearest | 9 | Y | 8 | 8 | 20-25 | 20-25 seconds | ||
| CK-43P-23L | Film, Poly, Metal | 10 | Y | 8 | 6 | 20-25 | 20-25 seconds | ||